ABS电瓶壳专用料 自产

牌号自产厂家(产地)自产用途级别注塑级

长期供应abs电瓶壳料

物性数据

数据提供企业 东莞市锦成塑胶原料有限公司性能项目测试条件测试方法数值/描述单位机械性能拉伸强度(引张强度)
ASTM D638/ISO 52744kg/cm²(MPa)[Lb/in2]断裂伸长率
ASTM D638/ISO 527
%拉伸模量
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in2]拉伸屈服伸长率(延伸率)
ASTM D638/ISO 527
%拉伸断裂伸长率(延伸率)
ASTM D638/ISO 527
%弯曲模量(弯曲弹性率)
ASTM D790/ISO 1782350kg/cm²(MPa)[Lb/in2]弯曲强度
ASTM D790/ISO 17870kg/cm²(MPa)[Lb/in2]洛氏硬度
ASTM D785R-102
IZOD 缺口冲击强度1/4" 23℃ASTM D256/ISO 17911.5kg·cm/cm(J/M)ft·lb/in1/4" -30℃ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in1/8" 23℃ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in1/8" -30℃ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/inCharpy冲击强度23℃ （缺口）ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in-30℃（缺口）ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in23℃（无缺口）ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in-30℃（无缺口）ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in物性性能比重（密度）
ASTM D792/ISO 11831.05
成型收缩率
ASTM D955
%熔融指数（流动系数）200℃/5kgASTM D1238/ISO 113323.8g/10min220℃/10kgASTM D1238/ISO 1133
g/10min吸水率 23℃/24H
ASTM D570/ISO 62
%热性能热变形温度退火ASTM D648/ISO 7580℃（℉）未退火ASTM D648/ISO 75
℃（℉）维卡软化点
ASTM D1525/ISO R306
℃（℉）熔点
-
℃（℉）燃烧性（率）
UL94HB
线性膨胀系数
ASTM D696/ISO 11359
mm/mm.℃加工条件干燥条件
加工温度射嘴
205℃料筒前段
200℃料筒中段
205℃料筒后段
210℃熔体温度
℃模具温度
℃压力注塑压力
Mpa保压压力
Mpa背压
Mpa螺杆转速
rpm其他备注
颜色
特性黑色用途15|电子器材 配件 电瓶壳原料行情浮动不定，价格具体内容请致电电仪或者微信咨询，微信号同手机号    盛先生