PC/ABS 中国台湾奇美PC-345

PROPERTIES CONDITION PC-330 PC-345 PC-365 PC-385 UNITMETHOD 

PHYSICAL 

       Melt Flow Index 260℃/5kg 13 18 2020 cm3/10min ISO 1133 

Spiral Flow Length 

260℃,2mm V:50%, P:50% 

35 33 30 28 cm Chimei method 

Specific Gravity 23℃ 1.08 1.10 1.13 1.15 --- ISO 2039 MoldShrinkage  0.4~0.6 0.4~0.6 0.4~0.6 0.4~0.6 % ISO-2577 RockwellHardness 23℃ R-108 R-108 R-115 R-114 --- ISO 2039-2 CLTEFlow:23-55℃ 9.0E-06 8.5E-06 8.0E-05 7.5E-05 cm/cm/℃ ISO11359-2        MECHANICAL       Tensile Strength @ Yield 50mm/min 50 50 54 55 MPa ISO-527Tensile Strength @ Break 50mm/min 40 42 50 57 MPa ISO-527 TensileElongation @ Break 50mm/min 100 100 120 130 % ISO-527 FlexuralStrength 2mm/min 70 75 80 85 MPa ISO-178 Flexural Modulus 2mm/min2100 2100 2200 2300 MPa ISO-178 Izod Impact (3.2mm) Notched, 23℃ 4045 50 55 kJ/m2 ISO-180 Izod Impact (3.2mm) Notched, -30℃ 35 40 4545 kJ/m2 ISO-180 Charpy Impact (3.2mm) Notched, 23℃ 40 45 50 55kJ/m2 ISO-179 Charpy Impact (3.2mm) Notched, -30℃ 35 40 45 45 kJ/m2ISO-179         THERMAL       Heat Distortion Temp. （unannealed） 4.0mm,1.82Mpa 120℃/hr 8893 102 108 ℃ ISO-75 Vicat Softening Temp. （unannealed） 1kg, 50℃/hr5kg, 50℃/hr 116 106 125 110 125 ℃ ISO-306        FLAMMABILITY        FlameRating_HB  1.5 1.5 1.5 1.5 mm UL-94        PROCESSING PARAMETERS 

       Drying Temperature  80~10080~100 80~100 80~100 ℃  Drying Time  4 4 4 4 Hrs Barrel Temperature  230~270 230~270 230~270 240~280 ℃ Mold Temperature  50~100 50~100 50~100 50~100℃